Grade |
Highlights |
| ADT KP251 |
Low SET at 150℃ |
| ADT 249B
|
High SET, for Bitumen |
| ADT 503
|
Highest SET |
| ADT 802 |
For EPS, XPS, PU Foam |
| ADT FP |
Specially for PU Foam |
|
 |
 |
|
|
 |
|
 |
Expandable Graphite
| Product Name |
Mesh |
Purity
% |
Start Expansion Temperature
℃ |
Expansion Volume
ml/g |
Properties/Highlights |
| ADT 20 |
-200 |
≥94 |
180 |
≥20 |
Finest particle size, min 80% below 75mircon for coatings, impregnation |
| ADT 35 |
-100 |
≥95 |
180 |
≥35 |
Fine particle size, min80% below 150micron/100mesh |
| ADT 150 |
+150 |
≥92 |
175 |
≥150 |
Used in coating, glue, EPS,XPS foam |
| ADT 248 |
+50 |
≥92 |
180 |
≥200 |
Stronger char |
| ADT 249 |
+50 |
≥95 |
180 |
≥250 |
Standard product for all main applications |
| ADT 249B |
+50 |
≥92 |
200 |
≥200 |
Mainly used in Bitumen |
| ADT 802 |
+80 |
≥95 |
180 |
≥230 |
For main application in EPS, XPS foam, sealing strip and PU foam |
| ADT 251 |
+50 |
≥99 |
180 |
≥250 |
High purity, soft ash, for application require least instruments damage |
| ADT 252 |
+50 |
≥95 |
250 |
≥180 |
With application where extruder used |
| ADT 282 |
+80 |
≥92 |
250 |
≥130 |
Similar to ADT 252, finer particle |
| ADT 503 |
+50 |
≥95 |
300 |
≥170 |
Highest SET |
| ADT 803 |
+80 |
≥95 |
300 |
≥70 |
Similar to ADT 503, finer particle |
| ADT KP251 |
+50 |
≥99 |
130 |
≥230 |
Low SET, sulfur-free, soft ash, strong expansion at low and medium temp. |
| ADT FP |
+50 |
≥95 |
180 |
≥250 |
Super clean surface, for PU foam |
| ADT 350 |
+50 |
≥95 |
175 |
≥350 |
Very high free expansion and expansion strength |
| ADT 351 |
+50 |
≥98 |
175 |
≥350 |
High purity, very high free expansion and expansion strength |
| ADT 400 |
+50 |
≥98 |
170 |
≥400 |
Highest free expansion and expansion strength, soft ash |
|
| |
Superfine Graphite Powder
| Product Name |
Carbon Content |
Particle Size Distribution |
Package |
| ADT 005 |
90.0 - 99.5 % |
D10 1.5 - 2.5 um
D50 4 - 6 um
D90 8 - 11 um |
Net Weight: 11kg
In Composite Paper Bag |
| ADT 010 |
90.0 - 99.5 % |
D10 3 - 4 um
D50 8 - 10 um
D90 20 - 24 um |
Net Weight: 11kg
In Composite Paper Bag |
| ADT 015 |
90.0 - 99.5 % |
D10 4 - 6 um
D50 10 - 15 um
D90 25 - 40 um |
Net Weight: 13kg
In Composite Paper Bag |
|
|
|